A wide variety of seamless and welded tubes are available in the market. ASTM B626 Welded Tube is among those many tubes. It is preferred over its seamless counterpart as it is cost-effective. This metal has nickel and cobalt chemistry due to which it has higher chances of cracking at a higher temperature. Therefore, the B626 specification mentions the standard for ASTM B626 Tubing so that it can reduce the risk of cracking at higher temperatures.
A control over carbon, titanium, and aluminum along with crystal grain in ASTM B626 UNS N10276 Welded Tube is obtained by heat treatment. Thus when exposed to high temperatures these tubes display excellent resistance to carburization and oxidation. These tubes have been modified to control rupturing property.
ASME SB 626 N06022 Tubing is manufactured using flat rolled alloy in an automatic welding process. They are used in condensers and heat exchangers as they have good resistance to heat. Also as per the specification, these tubes are provided in the solution annealed and descaled condition. Descaling provides a smooth finish whereas solution annealing dissolves the precipitation on it. We ensure that the ASTM B626 Hastelloy C22/C276 Welded Tube that we produce comply with all the standards mentioned in the specification. Thus assuring you of the quality of the final product that is being delivered to you is of good quality and is value for money. This transparency has helped us survive and gain respect in this industry and has put us among the leading manufacturers of ASME SB 626 N06022 Tubing.
Size | 6.00 mm OD up to 914.4 mm OD |
Thickness | 0.3mm – 50 mm, SCH 5, SCH10, SCH 40, SCH 80, SCH 80S, SCH 160, SCH XXS |
Length | Within 13500mm |
Type | Welded Pipes, Welded Tubes |
Hastelloy C276 | Ni | C | Mo | Mn | Si | Fe | P | S | Co | Cr |
Balance | 0.010 max | 15.00 – 17.00 | 1.00 max | 0.08 max | 4.00 – 7.00 | 0.04 max | 0.03 max | 2.5 max | 14.50 – 16.50 |
Density | Melting Point | Yield Strength (0.2%Offset) | Tensile Strength | Elongation |
8.89 g/cm3 | 1370 °C (2500 °F) | Psi – 52,000 , MPa – 355 | Psi – 1,15,000 , MPa – 790 | 40 % |
STANDARD | UNS | WERKSTOFF NR. | AFNOR | EN | JIS | BS | GOST |
Hastelloy C276 | N10276 | 2.4819 | – | NiMo16Cr15W | NW 0276 | – | ХН65МВУ |